coatingli 发表于 2004-6-24 19:24:00

金属-介质消偏振膜

<P>G/ZNS   28.00/AG   24.00ZNS   66.00/G</P><img src="data/attachment/forum/dvbbs/2004-6/2004624112411118.jpg" border="0" onload="if(this.width>screen.width*0.7) {this.resized=true; this.width=screen.width*0.7; this.alt=\'Click here to open new window\nCTRL+Mouse wheel to zoom in/out\';}" onmouseover="if(this.width>screen.width*0.7) {this.resized=true; this.width=screen.width*0.7; this.style.cursor=\'hand\'; this.alt=\'Click here to open new window\nCTRL+Mouse wheel to zoom in/out\';}" onclick="if(!this.resized) {return true;} else {window.open(\'data/attachment/forum/dvbbs/2004-6/2004624112411118.jpg\');}" onmousewheel="return imgzoom(this);" alt="" />

zz 发表于 2004-6-24 19:30:00

不错，不知牢固度如何？

coatingli 发表于 2004-6-25 01:47:00

<P>物理厚度，单位nm</P>

Jesus 发表于 2004-6-24 22:08:00

<P>金属+介质的方法,看你的曲线吸收A5%吧?</P>

yh15430 发表于 2004-6-25 01:21:00

coatingli：你材料后面的数字是几何厚度吧？

yh15430 发表于 2004-6-25 06:39:00

回复：（coatingli）物理厚度，单位nm

<P>非常感谢！</P>

likeoe 发表于 2004-6-25 10:09:00

<DIV class=quote><B>以下是引用<I>Jesus</I>在2004-6-24 14:08:18的发言：</B>

<P>金属+介质的方法,看你的曲线吸收A5%吧?</P></DIV>
<P>怎么看出来的？？？</P>

zz 发表于 2004-6-25 19:15:00

TFC上自动计算显示出的

jet 发表于 2004-6-28 06:33:00

七、八十年代用得很多。但现在普遍采用TiO2 或Ta2O5来替代ZnS，可以解决牢固度的问题。

zz 发表于 2004-6-28 16:32:00

这就是你不对了，你考虑AG的结合了吗？

缘睐汝痴 发表于 2011-10-26 16:44:55

谢谢

fql3310 发表于 2011-10-26 17:08:54

早期欧菲用介质膜代替AG了,听说镀80层左右.主要是因为吸收的缘故.国外有用到AG的,听说是改善了AG的工艺.效果非常理想.